White

• Very good adhesion to glass, steel, aluminium, PVC, melamine, etc. except for granular substrates or substrates coated with acrylic paint.

When applied to laminated monomeric or polymeric PVC films, the removable adhesives can become semi-permanent. The duration of application and the type of exposure may accelerate this phenomenon.

• In the case of painted substrates, self-adhesive media must only be applied to undamaged original paintwork. If the paintwork is not original and/or damaged, the application and the removal are at the judgement and risk of the installer.
• Minimum temperature recommended for film removal: 20 °C (68 °F).

If the temperature is lower, a heat gun can be used to facilitate the removal of the film.

Aanbevelingen

• The PVC film HX210WG2 is polymeric calendered in a similar way to the products of the 200 series. The estimated lifetime of the unlaminated, blank PVC film is 7 years if it is used under standard exposure conditions on a smooth, non-porous, properly prepared, non-degassing surface.
• The colour of the films is controlled by HEXIS in order to ensure faithful reproduction of their colour tints. Nevertheless, in the case that your project requires the use of several rolls, HEXIS recommend using only a single batch number of each reference.
• Optimal drying time for the inks before laminating or further processing is 24 hours minimum.
• The surface finish of the prints may be modified/improved/protected by applying the appropriate laminate: V750 or PC500. For UV prints, use the protective VCR750 laminate.

• Vertical outdoor exposure on flat, smooth and non-degassing surfaces:
  - up to 5 years.

• Removability on smooth and non-porous surfaces:
  - 2 to 3 years without significant traces of adhesive.

Beyond this period, the film can exhibit a behaviour similar to that of a film with a permanent adhesive.